Kawat baja untuk pembentukan kepala dingin SCM425

1. Komposisi kimia

Tabel 2-bahan kimia, unit %

Kelas baja	C	Si	Mn	P	S	Ni	Cr	Mo	Cu
SMn420	0.17 ~ 0.23	0.15 ~ 0.35	1.20 ~ 1.50	≤0.030	≤0.030	≤0.25	≤0.35	–	＜0.30
SMn433	0.30 ~ 0.36	0.15 ~ 0.35	1.20 ~ 1.50	≤0.030	≤0.030	≤0.25	≤0.35	–	＜0.30
SMn438	0.35 ~ 0.41	0.15 ~ 0.35	1.35 ~ 1.65	≤0.030	≤0.030	≤0.25	≤0.35	–	＜0.30
SMn443	0.40 ~ 0.46	0.15 ~ 0.35	1.35 ~ 1.65	≤0.030	≤0.030	≤0.25	≤0.35	–	＜0.30
SMnC420	0.17 ~ 0.23	0.15 ~ 0.35	1.20 ~ 1.50	≤0.030	≤0.030	≤0.25	0.35 ~ 0.70	–	＜0.30
SMnC443	0.40 ~ 0.46	0.15 ~ 0.35	1.35 ~ 1.65	≤0.030	≤0.030	≤0.25	0.35 ~ 0.70	–	＜0.30
SCr415	0.13 ~ 0.18	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	–	＜0.30
SCr420	0.18 ~ 0.23	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	–	＜0.30
SCr430	0.28 ~ 0.33	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	–	＜0.30
SCr435	0.33 ~ 0.38	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	–	＜0.30
SCr440	0.38 ~ 0.43	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	–	＜0.30
SCr445	0.43 ~ 0.48	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	–	＜0.30
SCM415	0.13 ~ 0.18	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	0.15 ~ 0.25	＜0.30
SCM418	0.16 ~ 0.21	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	0.15 ~ 0.25	＜0.30

Kelas baja	C	Si	Mn	P	S	Ni	Cr	Mo	Cu
SCM420	0.18 ~ 0.23	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	0.15 ~ 0.25	＜0.30
SCM421	0.17 ~ 0.23	0.15 ~ 0.35	0.70 ~ 1.00	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	0.15 ~ 0.25	＜0.30
SCM425	0.23 ~ 0.28	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	0.15 ~ 0.30	＜0.30
SCM430	0.28 ~ 0.33	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	0.15 ~ 0.30	＜0.30
SCM432	0.27 ~ 0.37	0.15 ~ 0.35	0.30 ~ 0.60	≤0.030	≤0.030	≤0.25	1.00 ~ 1.50	0.15 ~ 0.30	＜0.30
SCM435	0.33 ~ 0.38	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	0.15 ~ 0.30	＜0.30
SCM440	0.38 ~ 0.43	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	0.15 ~ 0.30	＜0.30
SCM445	0.43 ~ 0.48	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	0.15 ~ 0.30	＜0.30
SCM822	0.20 ~ 0.25	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	≤0.25	0.90 ~ 1.20	0.35 ~ 0.45	＜0.30
SNC236	0.32 ~ 0.40	0.15 ~ 0.35	0.50 ~ 0.80	≤0.030	≤0.030	1.00 ~ 1.50	0.50 ~ 0.90	–	＜0.30
SNC415	0.12 ~ 0.18	0.15 ~ 0.35	0.35 ~ 0.65	≤0.030	≤0.030	2.00 ~ 2.50	0.20 ~ 0.50	–	＜0.30
SNC631	0.27 ~ 0.35	0.15 ~ 0.35	0.35 ~ 0.65	≤0.030	≤0.030	2.50 ~ 3.00	0.60 ~ 1.00	–	＜0.30
SNC815	0.12 ~ 0.18	0.15 ~ 0.35	0.35 ~ 0.65	≤0.030	≤0.030	3.00 ~ 3.50	0.60 ~ 1.00	–	＜0.30
SNC836	0.32 ~ 0.40	0.15 ~ 0.35	0.35 ~ 0.65	≤0.030	≤0.030	3.00 ~ 3.50	0.60 ~ 1.00	–	＜0.30
SNCM220	0.17 ~ 0.23	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	0.40 ~ 0.70	0.40 ~ 0.60	0.15 ~ 0.25	＜0.30
SNCM240	0.38 ~ 0.43	0.15 ~ 0.35	0.70 ~ 1.00	≤0.030	≤0.030	0.40 ~ 0.70	0.40 ~ 0.60	0.15 ~ 0.30	＜0.30
SNCM415	0.12 ~ 0.18	0.15 ~ 0.35	0.40 ~ 0.70	≤0.030	≤0.030	1.60 ~ 2.00	0.40 ~ 0.60	0.15 ~ 0.30	＜0.30
SNCM420	0.17 ~ 0.23	0.15 ~ 0.35	0.40 ~ 0.70	≤0.030	≤0.030	1.60 ~ 2.00	0.40 ~ 0.60	0.15 ~ 0.30	＜0.30
SNCM431	0.27 ~ 0.35	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	1.60 ~ 2.00	0.60 ~ 1.00	0.15 ~ 0.30	＜0.30
SNCM439	0.36 ~ 0.43	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	1.60 ~ 2.00	0.60 ~ 1.00	0.15 ~ 0.30	≤0.30
SNCM447	0.44 ~ 0.50	0.15 ~ 0.35	0.60 ~ 0.90	≤0.030	≤0.030	1.60 ~ 2.00	0.60 ~ 1.00	0.15 ~ 0.30	≤0.30
SNCM616	0.13 ~ 0.20	0.15 ~ 0.35	0.80 ~ 1.20	≤0.030	≤0.030	2.80 ~ 3.20	1.40 ~ 1.80	0.40 ~ 0.60	≤0.30
SNCM625	0.20 ~ 0.30	0.15 ~ 0.35	0.35 ~ 0.60	≤0.030	≤0.030	3.00 ~ 3.50	1.00 ~ 1.50	0.15 ~ 0.30	≤0.30
SNCM630	0.25 ~ 0.35	0.15 ~ 0.35	0.35 ~ 0.60	≤0.030	≤0.030	2.50 ~ 3.50	2.50 ~ 3.50	0.50 ~ 0.70	≤0.30
SNCM815	0.12 ~ 0.18	0.15 ~ 0.35	0.30 ~ 0.60	≤0.030	≤0.030	4.00 ~ 4.50	0.70 ~ 1.00	0.15 ~ 0.30	≤0.30
SACM645	0.40 ~ 0.50	0.15 ~ 0.50	0.60 or less	≤0.030	≤0.030	≤0.25	1.30 ~ 1.70	0.15 ~ 0.30	≤0.30

Elemen yang tidak ditentukan dalam tabel ini tidak sengaja ditambahkan kecuali untuk tujuan penyelesaian baja cair.
Note a) tidak sengaja menambahkan.
b) Mo SNCM630 mungkin memiliki batas lebih rendah 0.30%, tergantung pada perjanjian antara pihak penerima.
c) Al SACM645 0.70% 1.20%.

3. Toleransi dimensi

Tabel toleransi 8 dimensi kawat hot rolled

Diameter	Toleransi diameter	Ketidakbulatan
<15	±0.3	<0.4
15<d≤25	±0.4	<0.5
25<d≤32	±0.5	<0.6
32<d≤50	±0.6	<0.7

Toleransi dimensi kawat dengan diameter lebih dari 50 mm tergantung pada perjanjian antara pihak penerima.
Note a) deviasi adalah perbedaan antara nilai maksimum dan nilai minimum diameter dalam potongan silang yang sama pada kawat.